Star Technology

E-65

E-65

Epoxy Tooling Board - 65 pcf

Compressive Strength (psi)

8000

Flexural Modulus (psi)

653000

Flexural Strength (psi)

20900

Shore Hardness

85D

Shrinkage Percent

N/A

Tensile Strength (psi)

7000

Filled

BC-30UV

BC-30UV

UV cure for symmetrical rotating assemblies

Cure Method

Heat

Pot Life/Gel Time

20 Seconds

Specific Gravity

1.85

Working Time

20 Seconds

BC-28

BC-28

Fast setting two part balancing compound

Cure Method

Room Temperature

Mix Ratio

1:1 by Weight or Volume

Pot Life/Gel Time

1 Hour

Specific Gravity

2.50g/cm³

Viscosity

Putty

Working Time

60 Minutes

BC-24

BC-24

VERY fast setting two part balancing compound

Cure Method

Room Temperature

Mix Ratio

1:1 by Weight or Volume

Pot Life/Gel Time

15 Minutes

Specific Gravity

2.50g/cm³

Viscosity

Putty

Working Time

15 Minutes

BC-22

BC-22

Cures overnight to a solid polymer which resists moisture and solvents

Cure Method

Room Temperature

Mix Ratio

1:1 by Weight or Volume

Pot Life/Gel Time

1 1/2 - 2 1/2 Hours

Viscosity

Putty

BC-178

BC-178

BC-28 with Extended Shelf Life

Cure Method

Room Temperature

Pot Life/Gel Time

1 Hour

Viscosity

Putty

BC-174

BC-174

BC-24 with Extended Shelf Life

Cure Method

Room Temperature

Mix Ratio

1:1 by Weight or Volume

Pot Life/Gel Time

15 Minutes

Viscosity

Putty

BC-172

BC-172

BC-22 with Extended Shelf Life

Cure Method

Room Temperature

Pot Life/Gel Time

1 1/2 - 2 1/2 Hours

Viscosity

Putty

BC-15

BC-15

No mix, fast cure, high specific gravity

Cure Method

Heat

Pot Life/Gel Time

2.5 Minutes

Specific Gravity

2.7

Viscosity

Putty

Working Time

2.5 Minutes

813-01

813-01

General Purpose Aluminum Filled Epoxy System

Compressive Strength (psi)

11400

Flexural Modulus (psi)

3.3x10-5

Flexural Strength (psi)

14200

Mixed Viscosity

380000

Mix Ratio

100:100

Pot Life/Gel Time

30

Shore Hardness

80D

Shrinkage Percent

nil

Tensile Strength (psi)

7000

Filled