Tooling

Epoxy Casting

524-01

524-01
Abrasion Resistant Surface Coat - Fast
Download TDS
Compressive Strength (psi)
14000
Flexural Modulus (psi)
148438
Flexural Strength (psi)
6140
Mixed Viscosity
15400
Mix Ratio
100:10
Pot Life/Gel Time
63
Shore Hardness
87D
Shrinkage Percent
0.00251
Tensile Strength (psi)
3879
Filled

533-01

533-01
Aluminum Filled Mass Casting - Slow
Download TDS
Compressive Strength (psi)
8300
Flexural Modulus (psi)
95192
Flexural Strength (psi)
6870
Mixed Viscosity
6100
Mix Ratio
100:12
Pot Life/Gel Time
198
Shore Hardness
87D
Shrinkage Percent
0.00129
Tensile Strength (psi)
3360
Filled

534-01

534-01
Abrasion Resistant Mass Casting - Slow
Download TDS
Compressive Strength (psi)
10500
Flexural Modulus (psi)
440000
Flexural Strength (psi)
6100
Mixed Viscosity
11700
Mix Ratio
100:12
Pot Life/Gel Time
150
Shore Hardness
86D
Shrinkage Percent
0.00166
Tensile Strength (psi)
3270
Filled

623-01

623-01
Aluminum Filled Casting - Fast
Download TDS
Compressive Strength (psi)
12000
Flexural Modulus (psi)
185114
Flexural Strength (psi)
6978
Mixed Viscosity
24400
Mix Ratio
100:7
Pot Life/Gel Time
50
Shore Hardness
87D
Shrinkage Percent
nil
Tensile Strength (psi)
3480
Filled

633-01

633-01
High Thermally Conductive Filled Casting
Download TDS
Compressive Strength (psi)
10000
Flexural Modulus (psi)
926000
Flexural Strength (psi)
6280
Mixed Viscosity
19000
Mix Ratio
100:9.3
Pot Life/Gel Time
100
Shore Hardness
80D
Shrinkage Percent
nil
Tensile Strength (psi)
3240
Filled

633-02

633-02
High Thermally Conductive Filled Casting
Download TDS
Compressive Strength (psi)
10000
Flexural Modulus (psi)
926000
Flexural Strength (psi)
6280
Mixed Viscosity
22000
Mix Ratio
100:9.3
Pot Life/Gel Time
64
Shrinkage Percent
nil
Tensile Strength (psi)
3240
Filled

523-01

523-01
Aluminum Filled Surface Casting - Fast
Download TDS
Compressive Strength (psi)
8540
Flexural Modulus (psi)
91814
Flexural Strength (psi)
6398
Mixed Viscosity
6400
Mix Ratio
100:10
Pot Life/Gel Time
82
Shore Hardness
86D
Shrinkage Percent
nil
Tensile Strength (psi)
3366
Filled

Epoxy Laminating

515-04

515-04
Laminating Paste-Fast
Download TDS
Compressive Strength (psi)
3520
Flexural Modulus (psi)
276000
Flexural Strength (psi)
7500
Mixed Viscosity
Paste
Mix Ratio
100:12
Pot Life/Gel Time
75
Shore Hardness
60D
Shrinkage Percent
nil
Tensile Strength (psi)
2400
Filled

515-06

515-06
Laminating Paste -Slow
Download TDS
Compressive Strength (psi)
3280
Flexural Modulus (psi)
46700
Flexural Strength (psi)
7100
Mixed Viscosity
Paste
Mix Ratio
100:12
Pot Life/Gel Time
120
Shore Hardness
60D
Shrinkage Percent
nil
Tensile Strength (psi)
2400
Filled

515-11

515-11
Laminating Putty
Download TDS
Mixed Viscosity
Putty
Mix Ratio
100:14
Pot Life/Gel Time
90
Shore Hardness
75D
Shrinkage Percent
nil
Filled

610-01

610-01
Aluminum Filled Laminating - Fast
Download TDS
Compressive Strength (psi)
13900
Flexural Modulus (psi)
109866
Flexural Strength (psi)
11064
Mixed Viscosity
50000
Mix Ratio
100:16
Pot Life/Gel Time
35
Shore Hardness
87D
Shrinkage Percent
0.01645
Tensile Strength (psi)
5547
Filled

610-04

610-04
Aluminum Filled Laminating - Slow
Download TDS
Compressive Strength (psi)
13540
Flexural Modulus (psi)
90800
Flexural Strength (psi)
13000
Mixed Viscosity
45000
Mix Ratio
100:14.5
Pot Life/Gel Time
52
Shore Hardness
87D
Shrinkage Percent
0.01645
Tensile Strength (psi)
5700
Filled

611-01

611-01
Clear Laminating - Fast
Download TDS
Compressive Strength (psi)
4300
Flexural Modulus (psi)
73455
Flexural Strength (psi)
16777
Mixed Viscosity
1300
Mix Ratio
100:19
Pot Life/Gel Time
37
Shore Hardness
86D
Shrinkage Percent
0.00461
Tensile Strength (psi)
5724
Unfilled

611-03

611-03
Clear Laminating - Medium
Download TDS
Compressive Strength (psi)
4300
Flexural Modulus (psi)
73455
Flexural Strength (psi)
16777
Mixed Viscosity
1300
Mix Ratio
100:20
Pot Life/Gel Time
45
Shore Hardness
80D
Shrinkage Percent
0.00461
Tensile Strength (psi)
5724
Unfilled

611-04

611-04
Clear Laminating - Slow
Download TDS
Compressive Strength (psi)
4300
Flexural Modulus (psi)
73455
Flexural Strength (psi)
16777
Mixed Viscosity
1000
Mix Ratio
100:19
Pot Life/Gel Time
55
Shore Hardness
78D
Shrinkage Percent
0.00461
Tensile Strength (psi)
5724
Filled

615-07

615-07
Laminating Putty
Download TDS
Mixed Viscosity
Putty
Mix Ratio
100:10
Pot Life/Gel Time
90
Shore Hardness
75D
Shrinkage Percent
nil
Filled

615-12

615-12
Laminating Putty
Download TDS
Mixed Viscosity
Putty
Mix Ratio
100:14
Pot Life/Gel Time
90
Shore Hardness
75D
Shrinkage Percent
nil
Filled

510-01

510-01
General Purpose Laminating
Download TDS
Compressive Strength (psi)
12900
Flexural Modulus (psi)
137218
Flexural Strength (psi)
9048
Mixed Viscosity
4500
Mix Ratio
100:16
Pot Life/Gel Time
25
Shore Hardness
86D
Shrinkage Percent
nil
Tensile Strength (psi)
4126
Filled

511-01

511-01
General Purpose Laminating
Download TDS
Compressive Strength (psi)
14200
Flexural Modulus (psi)
100000
Flexural Strength (psi)
8054
Mixed Viscosity
2000
Mix Ratio
100:25
Pot Life/Gel Time
20
Shore Hardness
84D
Shrinkage Percent
0.00347
Tensile Strength (psi)
3867
Unfilled

Epoxy Surface Coat

600-01

600-01
Black Polishable Surface - Fast
Download TDS
Compressive Strength (psi)
15300
Flexural Modulus (psi)
480000
Flexural Strength (psi)
14000
Mixed Viscosity
50000
Mix Ratio
100:18
Pot Life/Gel Time
30
Shore Hardness
86D
Shrinkage Percent
0.00144
Tensile Strength (psi)
5400
Filled

600-02

600-02
Black Polishable Surface - Slow
Download TDS
Compressive Strength (psi)
15300
Flexural Modulus (psi)
480000
Flexural Strength (psi)
14000
Mixed Viscosity
50000
Mix Ratio
100:19
Pot Life/Gel Time
60
Shore Hardness
80D
Shrinkage Percent
nil
Tensile Strength (psi)
5400
Filled

603-03

603-03
Aluminum Filled Surface Coat - Slow
Download TDS
Compressive Strength (psi)
11300
Flexural Modulus (psi)
136929
Flexural Strength (psi)
10980
Mixed Viscosity
56000
Mix Ratio
100:11
Pot Life/Gel Time
57
Shore Hardness
86D
Shrinkage Percent
nil
Tensile Strength (psi)
4089
Filled

603-04

603-04
Aluminum Filled Surface Coat - Fast
Download TDS
Compressive Strength (psi)
12000
Flexural Modulus (psi)
135000
Flexural Strength (psi)
12000
Mixed Viscosity
52000
Mix Ratio
100:13
Pot Life/Gel Time
35
Shore Hardness
86D
Shrinkage Percent
nil
Tensile Strength (psi)
4089
Filled

604-01

604-01
Styrene & Abrasion Resistant Surface Coat
Download TDS
Compressive Strength (psi)
14300
Flexural Modulus (psi)
664000
Flexural Strength (psi)
6500
Mixed Viscosity
164000
Mix Ratio
100:15
Pot Life/Gel Time
35
Shore Hardness
86D
Shrinkage Percent
0.0002
Tensile Strength (psi)
5400
Filled

502-01

502-01
Plastic Faced Plaster Surface Coat
Download TDS
Compressive Strength (psi)
12300
Flexural Modulus (psi)
122598
Flexural Strength (psi)
6355
Mixed Viscosity
100000
Mix Ratio
100:17
Pot Life/Gel Time
42
Shore Hardness
86D
Shrinkage Percent
nil
Tensile Strength (psi)
3503
Filled

503-01

503-01
Aluminum Filled Surface Coat
Download TDS
Compressive Strength (psi)
11000
Flexural Modulus (psi)
150000
Flexural Strength (psi)
2000
Mixed Viscosity
164000
Mix Ratio
100:11
Pot Life/Gel Time
55
Shore Hardness
86D
Shrinkage Percent
0.0428
Tensile Strength (psi)
6500
Filled

504-01

504-01
Abrasion Resistant Surface Coat
Download TDS
Compressive Strength (psi)
11700
Flexural Modulus (psi)
130000
Flexural Strength (psi)
6456
Mixed Viscosity
33800
Mix Ratio
100:10
Pot Life/Gel Time
36
Shore Hardness
86D
Shrinkage Percent
0.00037
Tensile Strength (psi)
3503
Filled

500-01

500-01
General Purpose Surface Coat - Slow
Download TDS
Compressive Strength (psi)
11700
Flexural Modulus (psi)
155950
Flexural Strength (psi)
7277
Mixed Viscosity
40000
Mix Ratio
100:16
Pot Life/Gel Time
25
Shore Hardness
87D
Shrinkage Percent
0.00116
Tensile Strength (psi)
2588

500-03

500-03
General Purpose Surface Coat - Fast
Download TDS
Compressive Strength (psi)
14900
Flexural Modulus (psi)
780000
Flexural Strength (psi)
7300
Mixed Viscosity
40000
Mix Ratio
100:23
Pot Life/Gel Time
25
Shore Hardness
87D
Shrinkage Percent
0.00124
Tensile Strength (psi)
2500

Fast Cast Urethane

230-05

230-05
Fast Cast Polyurethane
Download TDS
Compressive Strength (psi)
7300
Flexural Modulus (psi)
278000
Flexural Strength (psi)
3800
Mixed Viscosity
9000
Mix Ratio
100:13
Pot Life/Gel Time
15
Shore Hardness
82D
Shrinkage Percent
nil
Tensile Strength (psi)
1400

Miscellaneous

810-01

810-01
Durable Epoxy Model & Tooling Board
Download TDS
Compressive Strength (psi)
8000
Mixed Viscosity
18000
Mix Ratio
100:50
Pot Life/Gel Time
17
Shore Hardness
70D
Shrinkage Percent
nil
Tensile Strength (psi)
6000

811-01

811-01
General Purpose Epoxy Adhesive Rapid Cure
Download TDS
Compressive Strength (psi)
9800
Flexural Modulus (psi)
200000
Flexural Strength (psi)
6100
Mixed Viscosity
12000
Mix Ratio
100:100
Pot Life/Gel Time
5
Shore Hardness
80D
Shrinkage Percent
0.1142
Tensile Strength (psi)
2800

813-01

813-01
General Purpose Aluminum Filled Epoxy System
Download TDS
Compressive Strength (psi)
11400
Flexural Modulus (psi)
3.3x10-5
Flexural Strength (psi)
14200
Mixed Viscosity
380000
Mix Ratio
100:100
Pot Life/Gel Time
30
Shore Hardness
80D
Shrinkage Percent
nil
Tensile Strength (psi)
7000
Filled

Tooling Board

E-65

E-65
Epoxy Tooling Board - 65 pcf
Download TDS
Compressive Strength (psi)
8000
Flexural Modulus (psi)
653000
Flexural Strength (psi)
20900
Shore Hardness
85D
Shrinkage Percent
N/A
Tensile Strength (psi)
7000
Filled

E-90

E-90
Epoxy Tooling Board - 90 pcf
Download TDS
Compressive Strength (psi)
8000
Flexural Modulus (psi)
653000
Flexural Strength (psi)
20900
Shore Hardness
85D
Shrinkage Percent
N/A
Tensile Strength (psi)
7000
Filled

Urethane Potting

740-01A

740-01A
Shore 40A Optically Clear Urethane
Download TDS
Mixed Viscosity
750
Mix Ratio
100:98
Pot Life/Gel Time
12
Shore Hardness
40A
Shrinkage Percent
nil
Tensile Strength (psi)
475

755-01A

755-01A
Shore 55A Urethane
Download TDS
Mixed Viscosity
1000
Mix Ratio
100:27
Pot Life/Gel Time
30
Shore Hardness
55A
Shrinkage Percent
0.00571
Tensile Strength (psi)
475

770-01D

770-01D
High Impact Resistant Urethane
Download TDS
Mixed Viscosity
8500
Mix Ratio
100:75
Pot Life/Gel Time
30
Shore Hardness
70D
Shrinkage Percent
nil
Tensile Strength (psi)
8470

775-01A

775-01A
Shore 75A Urethane
Download TDS
Mixed Viscosity
700
Mix Ratio
100:34.1
Pot Life/Gel Time
6
Shore Hardness
77A
Shrinkage Percent
0.00142
Tensile Strength (psi)
2840

720-01A

720-01A
Shore 20 A Urethane - Slow
Download TDS
Mixed Viscosity
1800
Mix Ratio
100:120
Pot Life/Gel Time
10
Shore Hardness
20A
Shrinkage Percent
0.0078
Tensile Strength (psi)
162

720-02A

720-02A
Shore 20A Urethane - Fast
Download TDS
Mixed Viscosity
1800
Mix Ratio
100:120
Pot Life/Gel Time
10
Shore Hardness
20A
Shrinkage Percent
0.0078
Tensile Strength (psi)
162

735-01A

735-01A
Shore 35A Urethane
Download TDS
Mixed Viscosity
7000
Mix Ratio
100:27
Pot Life/Gel Time
15
Shore Hardness
35A
Shrinkage Percent
0.00249
Tensile Strength (psi)
361