Epoxy Laminating

Epoxy Laminating

610-04

610-04

Aluminum Filled Laminating - Slow

Compressive Strength (psi)

13540

Flexural Modulus (psi)

90800

Flexural Strength (psi)

13000

Mixed Viscosity

45000

Mix Ratio

100:14.5

Pot Life/Gel Time

52

Shore Hardness

87D

Shrinkage Percent

0.01645

Tensile Strength (psi)

5700

Filled

611-01

611-01

Clear Laminating - Fast

Compressive Strength (psi)

4300

Flexural Modulus (psi)

73455

Flexural Strength (psi)

16777

Mixed Viscosity

1300

Mix Ratio

100:19

Pot Life/Gel Time

37

Shore Hardness

86D

Shrinkage Percent

0.00461

Tensile Strength (psi)

5724

Unfilled

611-03

611-03

Clear Laminating - Medium

Compressive Strength (psi)

4300

Flexural Modulus (psi)

73455

Flexural Strength (psi)

16777

Mixed Viscosity

1300

Mix Ratio

100:20

Pot Life/Gel Time

45

Shore Hardness

80D

Shrinkage Percent

0.00461

Tensile Strength (psi)

5724

Unfilled

611-04

611-04

Clear Laminating - Slow

Compressive Strength (psi)

4300

Flexural Modulus (psi)

73455

Flexural Strength (psi)

16777

Mixed Viscosity

1000

Mix Ratio

100:19

Pot Life/Gel Time

55

Shore Hardness

78D

Shrinkage Percent

0.00461

Tensile Strength (psi)

5724

Filled

615-07

615-07

Laminating Putty

Mixed Viscosity

Putty

Mix Ratio

100:10

Pot Life/Gel Time

90

Shore Hardness

75D

Shrinkage Percent

nil

Filled

615-12

615-12

Laminating Putty

Mixed Viscosity

Putty

Mix Ratio

100:14

Pot Life/Gel Time

90

Shore Hardness

75D

Shrinkage Percent

nil

Filled

515-04

515-04

Laminating Paste-Fast

Compressive Strength (psi)

3520

Flexural Modulus (psi)

276000

Flexural Strength (psi)

7500

Mixed Viscosity

Paste

Mix Ratio

100:12

Pot Life/Gel Time

75

Shore Hardness

60D

Shrinkage Percent

nil

Tensile Strength (psi)

2400

Filled

515-06

515-06

Laminating Paste -Slow

Compressive Strength (psi)

3280

Flexural Modulus (psi)

46700

Flexural Strength (psi)

7100

Mixed Viscosity

Paste

Mix Ratio

100:12

Pot Life/Gel Time

120

Shore Hardness

60D

Shrinkage Percent

nil

Tensile Strength (psi)

2400

Filled

515-11

515-11

Laminating Putty

Mixed Viscosity

Putty

Mix Ratio

100:14

Pot Life/Gel Time

90

Shore Hardness

75D

Shrinkage Percent

nil

Filled

610-01

610-01

Aluminum Filled Laminating - Fast

Compressive Strength (psi)

13900

Flexural Modulus (psi)

109866

Flexural Strength (psi)

11064

Mixed Viscosity

50000

Mix Ratio

100:16

Pot Life/Gel Time

35

Shore Hardness

87D

Shrinkage Percent

0.01645

Tensile Strength (psi)

5547

Filled

510-01

510-01

General Purpose Laminating

Compressive Strength (psi)

12900

Flexural Modulus (psi)

137218

Flexural Strength (psi)

9048

Mixed Viscosity

4500

Mix Ratio

100:16

Pot Life/Gel Time

25

Shore Hardness

86D

Shrinkage Percent

nil

Tensile Strength (psi)

4126

Filled

511-01

511-01

General Purpose Laminating

Compressive Strength (psi)

14200

Flexural Modulus (psi)

100000

Flexural Strength (psi)

8054

Mixed Viscosity

2000

Mix Ratio

100:25

Pot Life/Gel Time

20

Shore Hardness

84D

Shrinkage Percent

0.00347

Tensile Strength (psi)

3867

Unfilled