Epoxy Casting

Epoxy Casting

523-01

523-01

Aluminum Filled Surface Casting - Fast

Compressive Strength (psi)

8540

Flexural Modulus (psi)

91814

Flexural Strength (psi)

6398

Mixed Viscosity

6400

Mix Ratio

100:10

Pot Life/Gel Time

82

Shore Hardness

86D

Shrinkage Percent

nil

Tensile Strength (psi)

3366

Filled

524-01

524-01

Abrasion Resistant Surface Coat - Fast

Compressive Strength (psi)

14000

Flexural Modulus (psi)

148438

Flexural Strength (psi)

6140

Mixed Viscosity

15400

Mix Ratio

100:10

Pot Life/Gel Time

63

Shore Hardness

87D

Shrinkage Percent

0.00251

Tensile Strength (psi)

3879

Filled

533-01

533-01

Aluminum Filled Mass Casting - Slow

Compressive Strength (psi)

8300

Flexural Modulus (psi)

95192

Flexural Strength (psi)

6870

Mixed Viscosity

6100

Mix Ratio

100:12

Pot Life/Gel Time

198

Shore Hardness

87D

Shrinkage Percent

0.00129

Tensile Strength (psi)

3360

Filled

534-01

534-01

Abrasion Resistant Mass Casting - Slow

Compressive Strength (psi)

10500

Flexural Modulus (psi)

440000

Flexural Strength (psi)

6100

Mixed Viscosity

11700

Mix Ratio

100:12

Pot Life/Gel Time

150

Shore Hardness

86D

Shrinkage Percent

0.00166

Tensile Strength (psi)

3270

Filled

623-01

623-01

Aluminum Filled Casting - Fast

Compressive Strength (psi)

12000

Flexural Modulus (psi)

185114

Flexural Strength (psi)

6978

Mixed Viscosity

24400

Mix Ratio

100:7

Pot Life/Gel Time

50

Shore Hardness

87D

Shrinkage Percent

nil

Tensile Strength (psi)

3480

Filled

633-01

633-01

High Thermally Conductive Filled Casting

Compressive Strength (psi)

10000

Flexural Modulus (psi)

926000

Flexural Strength (psi)

6280

Mixed Viscosity

19000

Mix Ratio

100:9.3

Pot Life/Gel Time

100

Shore Hardness

80D

Shrinkage Percent

nil

Tensile Strength (psi)

3240

Filled

633-02

633-02

High Thermally Conductive Filled Casting

Compressive Strength (psi)

10000

Flexural Modulus (psi)

926000

Flexural Strength (psi)

6280

Mixed Viscosity

22000

Mix Ratio

100:9.3

Pot Life/Gel Time

64

Shrinkage Percent

nil

Tensile Strength (psi)

3240

Filled